Method for Manufacturing Image Sensor

ABSTRACT

A method for manufacturing an image sensor includes forming a photolithography key in a scribe lane of a first substrate over which circuitry is formed in an active region. A photodiode is formed on an active region of a second substrate. The second substrate is bonded to the first substrate such that the photodiode is electrically connected to the circuitry. The photolithography key in the scribe lane of the first substrate is opened. A pattern is formed on the active region of the bonded second substrate using the opened photolithography key on/over the first substrate.

The present application claims priority under 35 U.S.C. § 119 to KoreanPatent Application No. 10-2007-0139393 (filed Dec. 27, 2007), which ishereby incorporated by reference in its entirety.

BACKGROUND

An image sensor is a semiconductor device for converting an opticalimage into an electric signal. The image sensor may be generallyclassified into a charge coupled device (CCD) image sensor and acomplementary metal oxide silicon (CMOS) image sensor (CIS).

A CIS may include a photodiode and a MOS transistor formed in a unitpixel, and generally obtains an image by sequentially detectingelectrical signals of unit pixels in a switching manner.

In a related art CIS structure, the photodiode and the transistor arehorizontally arranged.

Although the related art horizontal-type CIS has addressed some of thelimitations of CCD image sensors, a conventional horizontal-type CISimage sensor still has several problems.

For example, in a conventional horizontal-type CIS, a photodiode and atransistor are horizontally formed adjacent to each other on asubstrate. Therefore, an additional region for forming the photodiode isrequired, which may decrease the fill factor and limit the possibilityof resolution.

Also, in the conventional horizontal-type CIS, it is very difficult tooptimize processing by concurrently forming the photodiode and thetransistor.

SUMMARY

Embodiments of the present invention relate to a method formanufacturing an image sensor that integrates circuitry and aphotodiode.

Embodiments of the present invention relate to a method formanufacturing an image sensor in which a first substrate over which apattern is formed, and a second substrate, are bonded to manufacture avertical type image sensor. Prior to bonding the first substrate and thesecond substrate, a photolithography alignment key formed on and/or overthe first substrate is used to align the first substrate with the secondsubstrate.

The present method generally includes the following steps: forming aphotolithography key in a scribe lane of a first substrate; preparingthe first substrate over which a circuitry is formed on an activeregion; forming a photodiode on an active region of a second substrate;bonding the second substrate to the first substrate such that thephotodiode is electrically connected to the circuitry; opening thephotolithography key of the scribe lane of the first substrate; andforming a pattern on the active region of the bonded second substrateusing the opened photolithography key of the first substrate.

DRAWINGS

FIG. 1 illustrates a pixel region of an image sensor in accordance withexemplary embodiments of the present invention.

FIGS. 2 and 3 illustrate a scribe lane of an image sensor in accordancewith exemplary embodiments of the present invention.

DESCRIPTION

A method for manufacturing an image sensor in accordance withembodiments will be described in detail with reference to theaccompanying drawings.

FIG. 1 illustrates a pixel region of an image sensor in accordance withthe present method.

As illustrated in FIG. 1, an image sensor manufactured in accordancewith embodiments of the present invention may include: a first substrate100 on and/or over which circuitry (not shown) including metalinterconnection 110 is formed; a dielectric layer 120 on and/or over thecircuitry; and a photodiode 210 contacting the dielectric layer 120,bonded to first substrate 100, and electrically connected to thecircuitry.

Photodiode 210 has a contact hole (H1) and can be electrically connectedto a contact, which may be formed in the contact hole (H1).

In various embodiments, after first substrate 100 and a second substrateare bonded, a precise alignment pattern may be obtained using aphotolithography key formed on and/or over the first substrate 100 so asto obtain a pattern for an active region of the second substrate. Inpreferred embodiments, the pattern formed on the active region of thesecond substrate is an active pattern.

That is, when first substrate 100 (over which a pattern is formed) andthe additional second substrate are bonded to manufacture a verticaltype image sensor, a photolithography alignment key that is formed onand/or over first substrate 100 may be opened, and a color filter, aprobe pad or the like can be precisely aligned and formed using thephotolithography alignment key.

A method for manufacturing an active region of an image sensor will nowbe described with reference to FIG. 1.

As illustrated in FIG. 1, a method for manufacturing an image sensoraccording to embodiments of the present invention may include preparinga first substrate 100 in which circuitry (not shown) including a metalinterconnection 110 is formed. Although circuitry of first substrate 100is not shown, a CIS in accordance with an exemplary embodiment can be a4-transistor CIS. However, the invention is not limited as such. Inother embodiments, the CIS may comprise 5 transistors, 3 transistors, orany other number of transistors known in the art.

The metal interconnection formed in first substrate 100 may include ametal (not shown) and/or a plug (not shown). The metal may comprisesputter-deposited aluminum or aluminum alloy (e.g., Al with up to 4 wt.% Cu, up to 2 wt. % Ti, and/or up to 1 wt. % Si), on conventionaladhesion and/or barrier layers (e.g., Ti and/or TiN, such as a TiN-on-Tibilayer), and/or covered by conventional adhesion, barrier, hillocksuppression, and/or antireflective layers (e.g., Ti, TiN, WN, TiW alloy,or a combination thereof, such as a TiN-on-Ti bilayer or a TiW-on-Tibilayer). The plug may comprise tungsten (deposited by chemical vapordeposition [CVD]) or aluminum or aluminum alloy (e.g., as describedabove, deposited by sputtering), on conventional adhesion and/or barrierlayers (e.g., Ti and/or TiN, such as a TiN-on-Ti bilayer). The Ti, TiNand TiW layers may be deposited by CVD or sputtering.

Thereafter, a dielectric layer 120 is formed on and/or over firstsubstrate 100 such that dielectric 120 selectively contacts the metalinterconnection 110. In exemplary embodiments, the dielectric layer 120can be, but is not limited to, an oxide layer such as SiO₂.

In some embodiments, the dielectric layer 120 may comprise a pluralityof dielectric layers (e.g., silicon dioxide, silicon nitride, orcombinations thereof). Each of the plurality of dielectric layers maycorrespond to the metal and/or plug of the metal interconnection.Furthermore, each dielectric layer may comprise a lowermost, conformaletch stop layer (e.g., silicon nitride), a conformal buffer and/orgap-fill layer (e.g., silicon-rich oxide [SRO], TEOS [e.g., a siliconoxide formed by CVD from tetraethyl orthosilicate and oxygen], anundoped silicate glass [USG] or a combination thereof), a bulkdielectric layer (e.g., one or more silicon oxide layers doped withfluorine [e.g., a fluorosilicate glass or FSG], boron and/or phosphorus[BSG, PSG and/or BPSG]), and a capping layer (e.g., of TEOS, USG, aplasma silane [e.g., silicon dioxide formed by plasma-assisted CVD ofsilicon dioxide from silane and oxygen], or a combination thereof, suchas a bilayer of plasma silane on USG or TEOS, or a bilayer of USG onTEOS). A planarizing process, such as chemical mechanical polishing(CMP), may be subsequently performed on for dielectric layer 120.

The present method for manufacturing an image sensor can enhance thebonding force between the photodiode 210 and the circuitry by formingdielectric 120 between photodiode 210 and the circuitry. Also, thepresent method for manufacturing an image sensor can further improvebonding and cleaving states by forming dielectric on the substrate overwhich circuitry is formed, planarizing the dielectric through a CMP, andperforming a bonding process to minimize a height difference.

Next, a crystalline semiconductor layer (not shown) is formed on and/orover the second substrate (not shown). A photodiode is formed in thecrystalline semiconductor layer, so that defects in the photodiode maybe prevented.

For example, the crystalline semiconductor layer may be formed by anepitaxial growth method on and/or over the second substrate. After that,hydrogen ion implantation layer may be formed by implanting hydrogenions between the second substrate and the crystalline semiconductorlayer. After that, impurity ions are implanted into the crystallinesemiconductor layer to form photodiode 210.

In exemplary embodiments, a second conductive-type conduction layer 216may be formed in an upper portion of the crystalline semiconductorlayer. For example, a high concentration P-type conduction layer 216 canbe formed in the upper portion of the crystalline semiconductor layer byperforming a first blanket-ion implantation onto the entire surface ofthe second substrate without a mask. In some embodiments, the secondconductive-type conduction layer 216 can be formed at a junction depthof less than about 0.5 μm.

After that, a first conductive-type conduction layer 214 is formed undersecond conductive-type conduction layer 216. For example, a lowerconcentration N-type conduction layer 214 may be formed under secondconductive-type conduction layer 216 by performing a second blanket-ionimplantation onto the entire surface of second substrate 200 without amask. In one preferred embodiment, a low concentration N-type conductionlayer 214 is formed at a junction depth ranging from about 1.0 μm toabout 2.0 μm.

Also, embodiments may further include forming a high concentration firstconductive-type conduction layer 212 under the first conductive-typeconduction layer 214. In exemplary embodiments, the high concentrationfirst conductive-type conduction layer 212 can be a high concentrationN-type conduction layer, which can contribute to ohmic contact.

Next, the first substrate 100 and the second substrate are bonded suchthat photodiode 210 contacts the dielectric layer 120. In someembodiments, before the first substrate 100 and the second substrate arebonded to each other, the surface energy of the surface(s) to be bondedcan be increased through activation by plasma.

Next, the hydrogen ion implantation layer formed in the second substrate200 can be changed into a hydrogen gas layer by performing a heattreatment process on the second substrate. A lower portion of the secondsubstrate can be easily removed near the hydrogen gas layer so that thephotodiode 210 can be exposed.

Next, an etching process for separating photodiode 210 for each unitpixel is performed. For example, a contact hole (H1) selectivelyexposing metal interconnection 110 may be formed by removing acorresponding portion of photodiode 210 and dielectric 120 positioned ata boundary between pixels.

After that, a contact plug may be formed in the contact hole (H1), andthen processes for forming an upper electrode (not shown) and a colorfilter (not shown) may be performed.

Embodiments of the present invention result in forming a precisealignment pattern using the photolithography key formed on and/or overthe first substrate 100 as a pattern of the active region of the secondsubstrate after the first substrate 100 and the second substrate arebonded to each other.

That is, in exemplary embodiments, when the first substrate 100 (overwhich a pattern is formed) and the second substrate are bonded tomanufacture a vertical type image sensor, a photolithography alignmentkey formed on and/or over first substrate 100 is opened, and a colorfilter, a probe pad or the like can be precisely aligned and formedusing the photolithography alignment key.

Hereinafter, an exemplary process for opening a photolithography key inthe scribe lane of an image sensor will be described with reference toFIGS. 2 and 3.

First, photolithography key 110 p is formed in the scribe lane of afirst substrate 100.

After that, a second substrate 200 and the first substrate 100 arebonded to each other such that a photodiode (e.g., structure 210 ofFIG. 1) of the second substrate is electrically connected to thecircuitry of the first substrate 100.

After that, as illustrated in FIG. 2, a key open pattern 310 for openingphotolithography key 110 p of the scribe lane of first substrate 100 isformed on the second substrate 200.

As illustrated in FIG. 3, a scribe lane of the second substrate 200 isselectively removed to open photolithography key 110 p of the firstsubstrate 100 using the key open pattern as an etch mask. Whendielectric layer 120 is formed between first substrate 100 and secondsubstrate 200, portions of the dielectric layer 120 may be selectivelyremoved.

After that, a predetermined pattern may be formed on the active regionof the bonded second substrate 200 by using opened photolithography key110 p of first substrate 100. For example, as illustrated in exampleFIG. 1, photodiode 210 and dielectric 120 can be selectively removed toprecisely form the contact hole (H1) such that the position where metalinterconnection 110 is formed is precisely exposed.

In the process of opening photolithography key 110 p of first substrate100, the scribe lane of the second substrate 200 may be selectivelyremoved with a width range of 100-400 μm. For example, the scribe lanemay be removed at a width of 300 μm but is not limited as such. In otherembodiments the scribe lane may be removed at a width of 100 μm, 200 μm,250 μm, or any other value or range of values therein.

Furthermore, in exemplary methods, the photolithography key 110 p formedin first substrate 100 may be opened using a reactive ion etching (RIE).

In some embodiments, the key open pattern may be formed using a notchalignment of the first and second substrates. In such embodiments, wherethe pre-alignment process is performed using only a notch, the alignmentequipment generally has a precision of less than 200 μm. Since secondsubstrate 200 additively bonded on first substrate 100 forms a stackedstructure, which becomes a photodiode through a subsequent process, thesecond substrate 200 is the portion necessary only for the pixel region.

Therefore, if the key open pattern having a width range of about 100-400μm is formed at a position of the photolithography key in the scribelane having a width of about 100 μm by a notch pre-alignment process,the position of the photolithography key is opened and the pixel regionis not opened.

That is, the opening width of the key open pattern can be determined bya range of a sum of the precision of the alignment equipment and thewidth of the photolithography key.

Thus, when an etching process is performed after the key open pattern isformed, the bonded substrate is opened only at the position of thephotolithography key as illustrated in FIG. 3 so that alignment can beeasily performed using the photolithography key.

In accordance with the present invention, when first substrate 100 overwhich a pattern is formed and the additional second substrate are bondedto manufacture a vertical type image sensor, a photolithographyalignment key formed on and/or over first substrate 100 is opened, andthen a color filter, a probe pad or the like can be precisely alignedand formed using the opened photolithography alignment key.

Any reference in this specification to “one embodiment,” “anembodiment,” “exemplary embodiment,” etc., means that a particularfeature, structure, or characteristic described in connection with theembodiment is included in at least one embodiment of the invention. Theappearances of such phrases in various places in the specification arenot necessarily all referring to the same embodiment. Further, when aparticular feature, structure, or characteristic is described inconnection with any embodiment, it is within the purview of one skilledin the art to effect such feature, structure, or characteristic inconnection with other embodiments.

Although embodiments have been described herein, it should be understoodthat numerous other modifications and embodiments can be devised bythose skilled in the art that will fall within the spirit and scope ofthe principles of this disclosure. More particularly, variations andmodifications are possible in the component parts and/or arrangements ofthe subject combination arrangement within the scope of the disclosure,the drawings and the appended claims. In addition to variations andmodifications in the component parts and/or arrangements, alternativeuses will also be apparent to those skilled in the art.

1. A method for manufacturing an image sensor comprising: forming aphotolithography key in a scribe lane of a first substrate over which acircuitry is formed on or in an active region; forming a photodiode onor over an active region of a second substrate; bonding the secondsubstrate to the first substrate such that the photodiode iselectrically connected to the circuitry; opening the photolithographykey on the first substrate; and forming a pattern on the active regionof the bonded second substrate using the opened photolithography key. 2.The method of claim 1, wherein opening the photolithography keycomprises forming a key open pattern over the second substrate.
 3. Themethod of claim 2, wherein opening the photolithography key comprisesselectively removing the scribe lane of the second substrate using thekey open pattern as an etch mask.
 4. The method of claim 2, whereinforming the key open pattern is performed using a notch alignment of thefirst substrate and the second substrate.
 5. The method of claim 3,wherein forming the key open pattern is performed using a notchalignment of the first substrate and the second substrate.
 6. the methodof claim 3, wherein a width of the scribe lane of the second substratein a range of 100-400 μm is removed
 7. The method of claim 4, wherein awidth of the scribe lane of the second substrate in a range 100-400 μmis removed.
 9. The method of claim 1, wherein the pattern formed on theactive region of the second substrate is an active pattern.
 10. Themethod of claim 2, wherein the pattern formed on the active region ofthe second substrate is an active pattern.
 11. The method of claim 3,wherein the pattern formed on the active region of the second substrateis an active pattern.
 12. The method of claim 1, further comprisingforming a metal interconnection on the first substrate.
 13. The methodof claim 12, wherein the metal interconnection comprises a metal layerand/or a plug.
 14. The method of claim 12, further comprising forming adielectric layer on the first substrate contacting the metalinterconnection.
 15. The method of claim 14, wherein the dielectriclayer comprises an oxide.
 16. The method of claim 1, wherein thephotodiode comprises a crystalline semiconductor layer on the secondsubstrate.
 17. The method of claim 16, wherein the crystallinesemiconductor layer is formed by epitaxial growth.
 18. The method ofclaim 16, further comprising forming a hydrogen ion implantation layerbetween the second substrate and the crystalline semiconductor layer.19. The method of claim 1, wherein the photodiode comprises at least onecontact hole for electrically connecting the photodiode to a contact inthe contact hole.